1100 販売用アルミシート: グレード, サイズと購入ガイド
1100 販売用アルミシート: グレード, サイズと購入ガイド
導入
1100 aluminum sheet is one of the most practical commercially pure aluminum plates you can buy: with a minimum 99.0% aluminum content and a small copper addition, it is slightly stronger than 1050/1060 while keeping excellent formability, 耐食性, weldability and thermal conductivity.
It is the default sheet for chemical equipment, cookware and deep-drawn parts, ヒートシンク, signs and general fabrication that do not need high strength.
Offered factory-direct, 1100 sheet can be supplied in standard 4×8 ft and metric sizes or cut to your dimensions, with the temper and surface finish the product needs.
This guide covers the composition, プロパティ, sizes and weights, アプリケーション, 製造, と比べてどうですか 1050, 1060 そして 3003, そして注文方法.
とは何ですか 1100 アルミシート?
1100 is a non-heat-treatable 1xxx-series alloy strengthened only by cold work and softened by annealing. Sheet generally runs about 0.2–6 mm thick (thicker material is plate), supplied flat or cut to length. その特徴的な利点は、:
- 曲げ延性に優れる, スタンピング, スピニングと深絞り, 特にO型気質では.
- Very good atmospheric and chemical corrosion resistance from the self-healing oxide film.
- よりもわずかに高い強度 1050/1060 thanks to a controlled 0.05–0.20% copper addition.
- High thermal and electrical conductivity, plus excellent weldability and easy machining.
- ライト (について 2.71 g/cm3), rust-free and lower cost than alloyed grades; anodizes to a good film.
- The trade-off is modest strength; load-bearing or wear parts should use 3003, 5052 または 6061.
化学組成と機械的性質
制御された化学 (per ASTM B209 / ギガバイト/トン 3190) keeps silicon plus iron and copper within tight limits so forming, welding and corrosion performance stay high:
| 要素 | アル | そして + 鉄 | 銅 | ん | 亜鉛 |
| 1100 | ≧99.0 | ≤0.95 | 0.05–0.20 | ≤0.05 | ≤0.10 |
Mechanical properties change with temper, だから同じ 1100 シートは柔らかくて深絞り可能なシート、または硬くて硬いシートを提供できます (typical Rm values):
| 気性 | 引張 (MPa) | キャラクター |
| ○ (焼きなましされた) | 約. 75–110 | 最も柔らかい; 深い絵, 紡糸, 最大限の成形性 |
| H12 / H22 | 約. 95–125 | クォーターハード; ライトフォーミング |
| H14 / H24 | 約. 110–150 | ハーフハード; common general-purpose temper |
| H16 / H26 | 約. 135–170 | 4分の3ハード; より硬いパネル |
| H18 | 約. 150–200 | フルハード; 硬い, 限られた成形 |
値は厚さおよび規格によって若干異なります; confirm tensile and yield on the mill certificate for your gauge.
The small copper addition is what distinguishes 1100 in service.
It gives a modest but useful gain in strength without sacrificing the pure-aluminum forming that lets the sheet be drawn into deep pots and liners, and the metal still anodizes into a uniform, protective film used on trim and nameplates.
1100 thus occupies a deliberate middle ground—not as soft and conductive as 1060, but not as alloyed as 3003, which is why it appears so often in cookware, chemical and general-purpose stock.
標準サイズ, 表面と重量
1100 シートは約から生産されます 0.2 に 6 mm (プレートに 200 mm+ リクエストに応じて), およそまでの幅で 2600 mm と長さ 12,000 mm. Common sizes include 4×8 ft (1219×2438), 1000×2000, 1220×2440, 1250×2500 and 1500×3000, plus custom blanks to drawing.
| 表面 / 仕上げる | 一般的な使用方法 |
| ミル仕上げ (optional PVC/PVDF protective film) | 一般シート, 製造在庫, クラッディング |
| つや消し / 鏡 | 化粧パネル, 銘板, 点灯 |
| 陽極酸化 / カラーコーティングされた | Chemical and outdoor panels, durable signage, トリム |
| エンボス加工 / circles | 絶縁, anti-slip, cookware discs and deep-drawn parts |
Weight is easy at 2.71 g/cm3: kg/m² = 厚さ (mm) × 2.71; a 4×8 ft sheet covers about 2.972 ㎡.
| 厚さ | kg/平方メートル | 4×8シートあたりの重量 |
| 0.5 mm | 1.36 | 約. 4.0 kg |
| 1.0 mm | 2.71 | 約. 8.1 kg |
| 1.5 mm | 4.07 | 約. 12.1 kg |
| 2.0 mm | 5.42 | 約. 16.1 kg |
| 3.0 mm | 8.13 | 約. 24.2 kg |
代表的な用途
- 化学プロセス装置, 貯蔵タンク, 船舶, pipes and fittings that need corrosion resistance and weldability.
- 調理器具, cooking utensils and deep-drawn or spun parts, plus aluminum circles for pots and pans.
- ヒートシンク, ランプリフレクター, ボトルキャップストック, printing plates and food packaging components.
- 標識, nameplates and decorative or anodized architectural trim, and general stamped or bent parts.
Fabrication and Surface Treatment
1100 cuts, shears, bends and forms readily and can be laser, plasma or water-jet cut, 刻印された, spun and drilled; it welds cleanly by common processes and takes anodizing, ブラッシング, polishing and coating well.
Use O temper for the deepest draws and harder tempers where the finished part must hold shape; generous bend radii and clean, oil-free surfaces help on high-speed lines.
1100 対 1050, 1060 そして 3003
| 学年 | 分. アル / 合金化 | 強さ | ベストフィット |
| 1050 | 99.50% アル | 低い | Most economical general sheet and cladding |
| 1060 | 99.60% アル | 低い | Best conductivity/reflectivity; signs and electrical parts |
| 1100 | 99.00% アル, 銅少々 | 低～中 | やや強め; 形にする, 溶接, 化学薬品, 調理器具 |
| 3003 | アル + ん (について 1.2%) | 中くらい | について 20% 強い; 床, tread, tougher cladding |
選ぶ 1100 when you need a little more strength and weldability than 1050/1060 with the same pure-aluminum forming and corrosion; にステップアップする 3003 for real added strength.
品質管理, Pricing and How to Order
QC covers thickness and flatness, 幅/長さおよび対角公差, surface quality and tensile/yield by temper and chemistry on the MTC; ISO 9001 mills support SGS/BV inspection.
Sheet is interleaved with protective film and packed on pallets or in cases with moisture-proof wrapping for export. 価格はアルミインゴットのベースに加工費を加えた金額となります。, with thinner/wider gauge, カスタムカット, 表面処理と少量追加コスト;
compare per ton and per finished blank on identical specs under FOB/CFR/CIF (一般的に 30% デポジット, 船荷証券との残高). 引用するには, 合金/調質を送る (1100), 厚さ, シートまたはブランクの寸法, 表面, 量, アプリケーションと宛先ポート.
Verify new material on production-gauge samples rather than photos: run the sheet through your forming, welding or cutting line at normal speed, 幅全体の厚さを測定します, inspect the surface and, for food or chemical use, confirm the compliance paperwork matches the lot.
A signed pre-production sample then becomes the receiving standard, and an integrated mill that rolls and finishes in-house will hold that standard more reliably across repeat orders than spot resellers.
よくある質問
Q: とは何ですか 1100 に使用されるアルミニウムシート?
あ: Chemical tanks, vessels and piping, cookware and deep-drawn parts, ヒートシンク, サイン, bottle cap and printing stock, and general fabrication needing formability and corrosion rather than high strength.
Q: どのくらい強いのか 1100 と比べて 1060 そして 3003?
あ: It is slightly stronger than 1050/1060 due to a small copper addition, しかし 3003 (マンガン) is about 20% 強い; H18 1100 reaches roughly 150–200 MPa tensile.
Q: どの気質を選択すればよいですか?
あ: O for deep drawing and spinning, H14/H24 for general sheet, H16/H26 for stiffer panels and H18 for the most rigid plate with little forming.
Q: What sizes and thicknesses are available?
あ: About 0.2–6 mm sheet in widths to roughly 2600 mm, 4×8 フィートおよびメートル規格を含む, with plate and cut-to-size blanks on request.
Q: Can it be welded, anodized and cut to size?
あ: Yes—1100 welds cleanly, anodizes and finishes well, and can be laser or sawn cut, bent and supplied as custom blanks with protective film.
Q: 4×8のシートの重さはどれくらいですか?
あ: だいたい 8.1 kgで 1 mm, 12.1 kgで 1.5 mm, 16.1 kgで 2 mmと 24.2 kgで 3 mm, kg/m² = 厚さを使用 (mm) × 2.71 以上 2.972 ㎡.
結論
1100 aluminum sheet is the slightly stronger, easy-to-fabricate pure-aluminum plate for chemical equipment, 調理器具, heat transfer and signs.
パネルの加工方法から質を指定, 厚みとカットサイズを固定する, choose the surface, 工場証明書で購入, 価格だけではなく公差と承認済みサンプルを重視.