1. Materia compositio 1100 aluminium coil maxime constat ex aluminio et exigua cupri parte, Pii, manganese et aliis elementis, dum 3003 aluminium coil maxime constat ex alumine et particula cupri et manganese.
| Materia compositio | 1100 aluminium coil | 3003 aluminium coil |
|---|---|---|
| Al | ≥99.0% | ≥96.0% |
| Cu | ≤0.05% | 0.05%-0.20% |
| Mn | — | 1.0%-1.5% |
| And | ≤0.60% | — |
| Fe | ≤0.05% | ≤0.70% |
| Zn | — | ≤0.10% |
| Of | — | — |
| Alii | ≤0.05% | ≤0.15% |
2. Densitas densitas 3003 aluminium coil paulo altius quam of * 1100 aluminium coil, 2.72g/cm et 2.70g/cm respectively.
3. Fortitudo Fortitudo 3003 aluminium gyros est altior quam of * 1100 Aluminium Cils, 140-180MPa et 110-130MPa respectively.
4. Corrosio resistentia resistentia corrosionis 3003 aluminium coil melius quam 1100 aluminium coil, maxime in humida environment, ejus corrosio resistentia magis prominentibus.
5. Processing perficientur In processui observantia 1100 aluminium coil melius quam 3003 aluminium coil, maxime in frigore opus. tamen, in processus observantia * 3003 aluminium coil est relative pauper, et faciles rugas producere superficies.
6. Weldability The weldability of 3003 aluminium coil melius quam 1100 aluminium coil, quod est aptum ad processum cudoneum.
7. Calor curatio perficiendi calor curatio perficiendi 1100 aluminium coil melius quam 3003 aluminium coil, proprietates autem materiae possunt immutari calefaciendo et infrigidando.
8. PERFUSORIUS 1100 aluminium coil habet humilis densitas et ad leve consilium adhiberi potest. Idonea est aliquibus productis quae pondus requirunt, ut elit components et vehiculis.
9. Applicationem agri 1100 aluminium gyros maxime in lucendi, aluminium specula, radiators et aliis agris, dum 3003 aluminium gyros late in automobiles, aerospace, constructione, electronics et aliis agris.
10. Pretium secundum materiam compositionis et processabilitatis variat.