5052 Karatasi ya Alumini ya H18 kwa Msingi wa Sega la Asali: Nguvu, Sizes and Standards

Utangulizi

When an aluminum honeycomb panel must carry real load, survive outdoor or marine service and stay flat for decades, the core is usually built from 5052 H18 aluminum foil rather than the softer, nafuu 3003.
5052 is an aluminum-magnesium alloy with far higher strength and excellent corrosion resistance, and the full-hard H18 temper gives the thin cell walls the rigidity needed for high compression and shear performance.

This guide explains why 5052 H18 foil is used for honeycomb cores, its composition and mechanical properties, how the foil is converted into a core, the cell sizes, densities and strength values to specify, viwango vya mtihani wa anga na ASTM, Jinsi 5052 kulinganisha na 3003 na 5056, na jinsi ya kuagiza kiwanda moja kwa moja.

Ni Nini 5052 Karatasi ya H18?

5052 ni aloi ya mfululizo wa 5xxx isiyoweza kutibika iliyo na takriban 2.2–2.8% ya magnesiamu pamoja na nyongeza ndogo ya kromiamu.; inaimarishwa na kazi ya baridi.

Hasira ya H18 inamaanisha kuwa foil imekuwa ngumu hadi hali yake ngumu bila kuchujwa., kwa hivyo iko kwenye ugumu wake. Foil ngumu ni bora kwa msingi kwa sababu:

• Kiini cha asali hubeba mgandamizo na kukata badala ya kuchorwa kwa kina, kwa hivyo inahitaji nguvu ya mavuno mengi ili kuzuia kuta za seli nyembamba kutoka kwa buckling.
• The foil ni kuchapishwa tu na adhesive node, zimepangwa, iliyokatwa na kupanuliwa-haijatengenezwa kwa ukali baada ya kuvingirisha, kwa hivyo urefu wa chini wa H18 sio shida.
• Kuta ngumu za H18 huweka sawa seli za hexagonal wakati wa upanuzi na ubonyezaji wa paneli na kuinua mgandamizo wa msingi uliokamilika na nguvu ya kukata..

H19 (ziada-ngumu) wakati mwingine hubainishwa kwa nyembamba sana, foil yenye nguvu ya juu, wakati H38 ni sawa na imetulia; H18 inasalia kuwa hasira ya kibiashara iliyojaa ngumu ya asali.

Muundo wa Kemikali na Sifa za Mitambo

Element	Mg	Cr	Fe	Na	Cu	Mn	Zn	Al
5052	2.2-2.8	0.15-0.35	≤0.40	≤0.25	≤0.10	≤0.10	≤0.10	usawa

 

Magnesiamu hutoa nguvu, kromiamu hudhibiti muundo wa nafaka na tabia ya kutu, na chuma na silicon huwekwa chini kwa ushupavu.

Tabia ya kawaida ya foil kwa hasira (maadili kupanda katika nyembamba, vipimo ngumu kabisa; baadhi ya mill kupima kuhusu 319 MPa tensile on 5052 Karatasi ya msingi ya H18):

Hasira	Tensile (MPa)	Mazao (MPa)	Elongation
O (Annealed)	takriban. 130-170	takriban. 50-90	18-25%
H14	takriban. 195-230	takriban. 140-170	7-12%
H18 (kamili kwa bidii)	takriban. 250-320	takriban. 215-305	takriban 2-7%

 

Msongamano ni kuhusu 2.68 g/cm³. Daima thibitisha mvutano, kiwango cha mavuno na urefu kwenye cheti cha kinu kwa kipimo halisi.

Kutoka Foil hadi Asali Core

Uzalishaji wa kibadilishaji huchapisha mistari sambamba ya kibandiko cha nodi kwenye foil, hukusanya karatasi nyingi, cures the block, slices it to core thickness and expands it into hexagonal cells.

Foil for 5052 cores typically runs about 0.03–0.13 mm (30–130 μm, commonly 0.04–0.06 mm); the foil is often chromated or otherwise conversion-coated to strengthen the adhesive node bonds and improve corrosion resistance.

Kigezo	Masafa ya kawaida
Unene wa foil	about 0.03–0.13 mm (kawaida 0.04 / 0.05 / 0.06 mm)
Cell size	1/4″ (6.4), 3/8″ (9.5), 1/2″ (12.7), 3/4″ (19), 1″ (25 mm)
Core thickness	about 5–200 mm (deeper on request)
Supply form	unexpanded block/strip or expanded slice; perforated or solid; slotted
Maximum sheet	commonly up to roughly 1200–2000 mm wide by 2000–3000 mm long

Core Density, Strength and Test Standards

Smaller cells and thicker foil raise density and strength. Indicative expanded-core values (exact figures depend on alloy, foil gauge and supplier):

Cell size	Msongamano (kg/m³)	Flatwise compression (MPa)	Crush strength (MPa)
1/4″	kuhusu 81	takriban. 0.47	takriban. 0.19
3/8″	kuhusu 54	takriban. 0.26	takriban. 0.08
1/2″	kuhusu 38	takriban. 0.14	takriban. 0.05
3/4″	kuhusu 30	takriban. 0.09	takriban. 0.03
1″	kuhusu 31	takriban. 0.05	takriban. 0.02

 

5052 cores deliver higher shear (pande zote mbili za utepe L na W zinazopita), uchovu na utendaji wa athari kuliko 3003 kwa msongamano sawa.

Viini vya anga vimehitimu kuwa AMS-C-7438 (zamani MIL-C-7438); Nguvu ya nodi-bondi inajaribiwa kwa ASTM C363, shear ya sahani kwa ASTM C273, ukandamizaji wa gorofa kwa ASTM C365 na kushikamana kwa uso kwa ASTM C297.

Bainisha kiwango na iwapo thamani za kawaida au za chini zaidi zinahitajika.

Maombi ya kawaida

• Ukuta wa usanifu wa pazia na paneli za asali za facade ambazo lazima zisalie na hali ya hewa nje.
• Ukuta wa reli na usafiri, paneli za sakafu na dari kwa treni za kasi na metro (uzani mwepesi, ngumu, sambamba na mahitaji ya moto).
• Sakafu za anga, mambo ya ndani na nyuso za udhibiti, pamoja na vichwa vingi vya baharini na samani ambapo upinzani wa chumvi ni muhimu.
• Makabati ya vifaa, vyumba safi na paneli za lifti, samani, miundo ya akustisk, upepo na sehemu nyepesi za magari.

5052 vs 3003 na 5056

Aloi / hasira	Mvutano wa foil	Nguvu	Kutu	Inafaa zaidi
3003 H18	takriban. 165- 200 MPa	Kati	Nzuri	Cores za usanifu wa kiuchumi na mapambo
5052 H18/H19	takriban. 250- 320 MPa	Juu	Bora kabisa	Nje, baharini, transit na cores miundo
5056 H18	juu tena	Juu sana	Bora kabisa	Cores za anga za juu kwa nguvu ya juu zaidi

 

Chagua 3003 kwa gharama katika vifuniko vya ndani au vya jumla, 5052 wakati nguvu, uchovu na kutu huendesha muundo, na 5056 ambapo utendakazi wa juu zaidi wa anga unahalalisha bei.

5052 huunda kwa urahisi kidogo kuliko 3003, lakini hii haina maana mara tu foil inapanuliwa kuwa msingi.

Vipimo, Mazao na Kuagiza

Karibu 2.68 g/cm³, g/m² = unene (μM) × 2.68, kwa hivyo eneo la foil kwa tani ni rahisi kukadiria kwa upangaji wa nyenzo:

Kipimo cha foil	g/m²	Takriban. m² kwa tani
30 μM	80	12,400
40 μM	107	9,330
50 μM	134	7,460
60 μM	161	6,220
100 μM	268	3,730

 

Udhibiti wa ubora unashughulikia uvumilivu wa kupima na upana, Ubora wa uso, mkazo/mavuno kwa hasira, kemia kwenye MTC na, kwa cores zilizokamilishwa, msongamano, dhamana ya nodi na maadili ya shear/compression, na ISO 9001 na ukaguzi wa SGS/BV unapatikana.

Ili kuagiza foil, tuma aloi na hasira (5052 H18), chachi, upana na vipimo vya roll, kitambulisho cha msingi, mahitaji ya chromate/mipako na wingi; kwa cores kumaliza kuongeza ukubwa wa seli, unene wa msingi, msongamano, fomu ya kawaida na iliyopanuliwa au ya kuzuia.

Masharti ya kawaida ni 30% kuweka na salio dhidi ya bili ya shehena, FOB/CFR/CIF.

Maswali Yanayoulizwa Mara Kwa Mara

Q.: Kwa nini utumie 5052 H18 foil badala ya 3003 kwa sega la asali?

A: 5052 H18 ina nguvu zaidi na uchovu bora na kutu (ikiwa ni pamoja na baharini) utendaji, kwa hivyo msingi hutoa mgandamizo wa hali ya juu na shear kwa nje, usafiri, paneli za baharini na za miundo; 3003 huchaguliwa hasa kwa gharama ya chini katika kufunika kwa jumla.

Q.: Kwa nini hasira kali ya H18?

A: Msingi unahitaji ugumu, kuta za seli zenye mavuno mengi na hazijachorwa kwa kina baada ya kuviringishwa, kwa hivyo foil kamili-ngumu huongeza mgandamizo na ukata huku ikiweka seli sare wakati wa upanuzi.

Q.: Ni unene gani wa foil na saizi ya seli ni ya kawaida?

A: Foil ya msingi kawaida huendesha 0.03-0.13 mm (mara nyingi 0.04-0.06 mm) na seli za 1/4″, 3/8″, 1/2″, 3/4″ au 1″; seli ndogo na foil thicker kutoa denser, cores zenye nguvu zaidi.

Q.: Ni viwango gani vinatumika?

A: Viini vya anga hutumia AMS-C-7438; dhamana ya nodi ni ASTM C363, shear ASTM C273, compression ASTM C365 and facing adhesion ASTM C297, with mill and core test certificates.

Q.: Do you supply foil only or finished cores?

A: Both—5052 H18 foil in jumbo or slit rolls for converters, and expanded or unexpanded finished honeycomb cores cut to cell size, density and thickness.

Q.: MOQ ni nini na wakati wa kuongoza?

A: Foil MOQ is commonly several tons per specification and finished cores depend on size and volume, with samples and trial orders available; lead time varies with gauge, quantity and coating.

Hitimisho

5052 H18 is the high-strength, corrosion-resistant foil behind premium aluminum honeycomb cores for architecture, rail, aerospace and marine use.

Its full-hard walls deliver the compression, shear and fatigue that 3003 cannot, while staying lighter and stiffer than almost any alternative.

Specify foil gauge, ukubwa wa seli, core density and the test standard, and buy on certificates and approved samples rather than price alone.